The format of your table looks correct to me.
You have set your bend radius to 0.5 for all thicknesses so this should work fine. Make sure your feature dialogs (flange, etc.) have the Bend Radius set to global factor so this value is read and all features will have the same bend radius.
If you would like to attached your standards file or send direct to me I can check and test it for you.
One further comment: Do you really want a fixed bend radius for all thicknesses? I'd suggest having 0.5 for all will not be possible in reality - the material will fracture. A bend radius of at least the material thickness is advised with Steel.